牌号
|
MgO/%
≥
|
SiO2/%
≤
|
CaO/%
≤
|
灼减/%
≤
|
CaO/SiO2摩尔比
|
颗粒体积密度/g·cm-3≥
|
|
MS-98A
|
97.7
|
0.3
|
0.30
|
≥3
|
3.40
|
|
|
MS-98B
|
97.7
|
0.4
|
0.30
|
≥2
|
3.35
|
|
|
MS-98C
|
97.5
|
0.4
|
0.30
|
≥2
|
3.30
|
|
|
MS-97A
|
97.0
|
0.5
|
0.30
|
≥2
|
3.40
|
|
|
MS-97B
|
97.0
|
0.6
|
0.30
|
≥2
|
3.35
|
|
|
MS-97C
|
97.0
|
0.8
|
0.30
|
3.30
|
||
|
MS-96A
|
96.0
|
1.0
|
0.30
|
3.30
|
||
|
MS-96B
|
96.0
|
1.5
|
0.30
|
3.25
|
||
|
MS-95A
|
95.0
|
2.0
|
1.6
|
0.30
|
3.25
|
|
|
MS-95B
|
95.0
|
2.2
|
1.6
|
0.30
|
3.20
|
|
|
MS-93A
|
93.0
|
3.0
|
1.6
|
0.30
|
3.20
|
|
|
MS-93B
|
93.0
|
3.5
|
1.6
|
0.30
|
3.18
|
|
|
MS-90A
|
90.0
|
4.0
|
1.6
|
0.30
|
3.20
|
|
|
MS-90B
|
90.0
|
4.8
|
2.0
|
0.30
|
3.18
|
|
|
MS-87
|
87.0
|
7.0
|
2.0
|
0.50
|
3.20
|
|
|
MS-84
|
84.0
|
9.0
|
2.0
|
0.50
|
3.20
|
|
|
MS-88
|
88.0
|
4.0
|
5.0
|
0.50
|
||
|
MS-83
|
83.0
|
5.0
|
5.0
|
0.80
|
注：MS-88及MS-83牌号为冶金用烧结镁砂。
烧结镁砂的颗粒组成要求：
0~30mm：其中小于1mm的不大于5%；
0~90mm：其中小于1mm的不大于8%；
0~120mm：其中大于120mm的不大于10%，小于1mm的不大于15%；
其他颗粒：供需双方商定。
烧结镁砂的外观质量：
MS-98、MS-97和MS-96牌号：不得混入欠烧品和杂质；
MS-93、MS-90、MS-87和MS-84牌号：粒度大于30mm者，含欠烧品、工业炉熔瘤和黑块的表面积分别不得超过该镁砂块表面积的1/3、1/3和1/4；粒度为5~30mm者，含欠烧品、熔瘤和黑块的表面积分别不得超过该镁砂块表面积的1/2；
MS-88和MS-83牌号：粒度大于30mm者，含欠烧品、熔瘤和黑块的表面积分别不得超过该镁砂块表面积的1/2；5~30mm者，不得是整块为欠烧品。
欠烧品和杂质的限制含量：
MS-98、97、96牌号：不准有欠烧品和杂质；
MS-95牌号：欠烧品和杂质含量不大于每批量的1%；
MS-93、90、87、84牌号：欠烧品和杂质含量不大于每批量的2%；
欠烧品和杂质中焦炭含量（以大于5mm者计）：MS-95、93、90、87、84牌号中不大于每批量的0.03%；其余牌号不大于每批量的0.04%。